TPEE DYM160 BK373 美国杜邦 TPEE高性能 高模量
性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTM D412/ISO 527kg/cm2(MPa)[Lb/in2]断裂伸长率ASTM D412/ISO 527%拉伸模量ASTM D412/ISO 527kg/cm2(MPa)[Lb/in2]拉伸断裂伸长率(延伸率)ASTM D412/ISO 527%拉伸屈服伸长率(延伸率)ASTM D412/ISO 527℃(℉)弯曲模量(弯曲弹性率)ASTM D790/ISO 178160kg/cm2(MPa)[Lb/in2]洛氏硬度ASTM D78553IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/inChapy冲击强度23℃ (缺口)ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in-30℃(缺口)ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in23℃(无缺口)ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in-30℃(无缺口)ASTM D2457kg·cm/cm(J/M)ft·lb/in撕裂强度ASTM D624/ISO 34kN/m物性性能比重(密度)ASTM D9551170%熔融指数(流动系数)200℃/5kgASTM D1238/ISO 1133g/10min220℃/10kgASTM D1238/ISO 1133g/10min吸水率 23℃/24HASTM D570/ISO 620.05%成型收缩率ASTM D955%热性能维卡软化点ASTM D1525/ISO R306170℃(℉)熔点-220℃(℉)燃烧性(率)UL94电气性能介电常数100HZASTM D150/IEC 602501MHZASTM D150/IEC 60250介电损耗100HZASTM D150/IEC 602501MHZASTM D150/IEC 60250体积电阻率ASTM D257/IEC 60093Ω.cm表面电阻率ASTM D257/IEC 60093Ω耐电弧性ASTM D495/IEC 60112加工条件干燥条件加工温度射嘴℃料筒前段℃料筒中段℃料筒后段℃熔体温度℃模具温度℃压力注塑压力Mpa保压压力Mpa背压Mpa螺杆转速pm其他备注颜色特性高性能,高模量用途适用于气囊门TPEE(热塑性聚酯弹性体)是含有聚酯硬段和聚醚软段的嵌段共聚物。其中聚醚软段和未结晶的聚酯形成无定形相聚酯硬段部分结晶形成结晶微区,起物理交联点的作用。TPEE具有橡胶的弹性和工程塑料的强度;软段赋予它弹性,使它象橡胶;硬段赋予它加工性能,使它象塑料;与橡胶相比,它具有更好的加工性能和更长的使用寿命;与工程料相比,同样具有强度高的特点,而柔韧性和动态力学性能更好。
生产企业:美国杜邦 牌号:DYM160 BK373 重量:25kg/包 包装:原厂原包
优异的抗弯曲疲劳性能· 极强的耐撕裂,抗蠕变性· 使用温度范围宽(-50--180℃)
· 良好的耐磨性能,回弹力好,反拨性高· 出色的耐冲击性能,尤其是在低温(-40℃)
· 极好的耐油及耐化学性能· 极佳的电气性能及电荷承受能力
· 可与PC、PVC、ABS、PBT、PET共混和粘结· 易加工,可以注塑、挤出、吹塑、和熔融铸塑
· 与油漆,胶水和金属均具有极好的粘结性· 硬度范围大(30D-82D),着色方便